| 規(guī)格級別 | 高密度,清晰度，高,食品接觸的合規(guī)性,均聚物,剛性，高,低速凝固晶點,阻隔樹脂 共擠出成型,薄膜擠出 | 外觀顏色 | |
| 該料用途 | 薄膜,混合,食品包裝 | ||
| 備注說明 | |||
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 | ASTMD792 | 0.958 | g/cm3 | |
| 物理性能 | 熔流率（熔體流動速率）(190°C/2.16kg) | ASTMD1238 | 0.95 | g/10min | |
| 薄膜 | 薄膜厚度-經(jīng)測試 | 38 | μm | ||
| 薄膜 | SecantModulus-1%Secant,MD(38μm,BlownFilm) | ASTMD882 | 840 | MPa | |
| 薄膜 | SecantModulus-1%Secant,TD(38μm,BlownFilm) | ASTMD882 | 1180 | MPa | |
| 薄膜 | TensileStrength-MD(Yield,38μm,BlownFilm) | ASTMD882 | 25.0 | MPa | |
| 薄膜 | TensileStrength-TD(Yield,38μm,BlownFilm) | ASTMD882 | 27.0 | MPa | |
| 薄膜 | TensileStrength-MD(Break,38μm,BlownFilm) | ASTMD882 | 42.0 | MPa | |
| 薄膜 | TensileStrength-TD(Break,38μm,BlownFilm) | ASTMD882 | 40.0 | MPa | |
| 薄膜 | TensileElongation-MD(Break,38μm,BlownFilm) | ASTMD882 | 560 | % | |
| 薄膜 | TensileElongation-TD(Break,38μm,BlownFilm) | ASTMD882 | 890 | % | |
| 薄膜 | 落錘沖擊(38μm,吹塑薄膜) | ASTMD1709A | 44 | g | |
| 薄膜 | ElmendorfTearStrength-MD(38μm,BlownFilm) | ASTMD1922 | 26 | g | |
| 薄膜 | 埃爾曼多夫抗撕強度-TD(38μm,吹塑薄膜) | ASTMD1922 | 710 | g | |
| 薄膜 | OxygenTransmissionRate(23°C,0%RH,38μm,BlownFilm) | ASTMD3985 | 1500 | cm3/m2/24hr | |
| 薄膜 | WaterVaporTransmissionRate(38°C,100%RH,38μm,BlownFilm) | ASTMF1249 | 2.6 | g/m2/24hr | |
| 硬度 | 肖氏硬度(邵氏D) | ASTMD2240 | 68 | ||
| 熱性能 | 維卡軟化溫度 | ASTMD1525 | 131 | °C | |
| 光學性能 | Gloss(45°,38.0μm,BlownFilm) | ASTMD2457 | 23 | ||
| 光學性能 | 霧度(38.0μm,吹塑薄膜) | ASTMD1003 | 36 | % | |
| ADDITIONAL INFORMATION | 補充信息 | TestMethod | NominalValue | Unit | |
| ADDITIONAL INFORMATION | LowFrictionPuncture-BlownFilm(38.0μm) | InternalMethod | 200 | J/cm | |