| 規(guī)格級別 | 可加工性，良好,抗結塊性,低密度,抗氧化性,光滑性 吹塑成型,吹塑薄膜,擠出 | 外觀顏色 | |
| 該料用途 | |||
| 備注說明 | |||
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 | ASTMD792 | 0.923 | g/cm3 | |
| 物理性能 | 熔流率（熔體流動速率）(190°C/2.16kg) | ASTMD1238 | 1.4 | g/10min | |
| 薄膜 | 薄膜厚度-經(jīng)測試 | 35 | μm | ||
| 薄膜 | 膜刺穿力(35μm) | ASTMD3420 | 4.90 | N | |
| 薄膜 | 抗張強度 | MD:斷裂,35μm | ASTMD882 | 34.0 | MPa |
| 薄膜 | 抗張強度 | TD:斷裂,35μm | ASTMD882 | 26.0 | MPa |
| 薄膜 | 伸長率 | MD:斷裂,35μm | ASTMD882 | 700 | % |
| 薄膜 | 伸長率 | TD:斷裂,35μm | ASTMD882 | 800 | % |
| 薄膜 | 埃爾曼多夫抗撕強度 | MD:35μm | ASTMD1922 | 250 | g |
| 薄膜 | 埃爾曼多夫抗撕強度 | TD:35μm | ASTMD1922 | 350 | g |
| 薄膜 | ImpactResistance,Film | ASTMD1709 | 190 | J/cm | |
| 薄膜 | Toughness,Film | MD | ASTMD882 | 130 | MPa |
| 薄膜 | Toughness,Film | TD | ASTMD882 | 145 | MPa |
| 薄膜 | 薄膜厚度-經(jīng)測試 | 35 | μm | ||
| 薄膜 | 膜刺穿力(35μm) | ASTMD3420 | 4.90 | N | |
| 薄膜 | 抗張強度 | MD:斷裂,35μm | ASTMD882 | 34.0 | MPa |
| 薄膜 | 抗張強度 | TD:斷裂,35μm | ASTMD882 | 26.0 | MPa |
| 薄膜 | 伸長率 | MD:斷裂,35μm | ASTMD882 | 700 | % |
| 薄膜 | 伸長率 | TD:斷裂,35μm | ASTMD882 | 800 | % |
| 薄膜 | 埃爾曼多夫抗撕強度 | MD:35μm | ASTMD1922 | 250 | g |
| 薄膜 | 埃爾曼多夫抗撕強度 | TD:35μm | ASTMD1922 | 350 | g |
| 薄膜 | ImpactResistance,Film | ASTMD1709 | 190 | J/cm | |
| 薄膜 | Toughness,Film | MD | ASTMD882 | 130 | MPa |
| 薄膜 | Toughness,Film | TD | ASTMD882 | 145 | MPa |
| 光學性能 | 透射率(35.0μm) | ASTMD1003 | 71.0 | % | |
| 光學性能 | 霧度(35.0μm) | ASTMD1003 | 24 | % | |