| 規(guī)格級別 | 外觀顏色 | ||
| 該料用途 | |||
| 備注說明 | |||
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.915 | g/cm3 | |
| 物理性能 | 熔流率（熔體流動速率）(190°C/2.16kg) | ASTMD1238 | 3.5 | g/10min | |
| 薄膜 | 薄膜厚度-經(jīng)測試 | 40 | μm | ||
| 薄膜 | 抗張強度 | MD:屈服,40μm,擠塑薄膜 | ASTMD882 | 10.0 | MPa |
| 薄膜 | 抗張強度 | TD:屈服,40μm,擠塑薄膜 | ASTMD882 | 9.00 | MPa |
| 薄膜 | 抗張強度 | MD:斷裂,40μm,擠塑薄膜 | ASTMD882 | 47.0 | MPa |
| 薄膜 | 抗張強度 | TD:斷裂,40μm,擠塑薄膜 | ASTMD882 | 49.0 | MPa |
| 薄膜 | 伸長率 | MD:斷裂,40μm,擠塑薄膜 | ASTMD882 | 630 | % |
| 薄膜 | 伸長率 | TD:斷裂,40μm,擠塑薄膜 | ASTMD882 | 700 | % |
| 薄膜 | 落錘沖擊2(40μm,鑄造薄膜) | ASTMD1709 | 700 | g | |
| 薄膜 | 埃爾曼多夫抗撕強度 | MD:40μm,鑄造薄膜 | ASTMD1922 | 12 | g |
| 薄膜 | 埃爾曼多夫抗撕強度 | TD:40μm,鑄造薄膜 | ASTMD1922 | 25 | g |
| 薄膜 | 薄膜厚度-經(jīng)測試 | 40 | μm | ||
| 薄膜 | 抗張強度 | MD:屈服,40μm,擠塑薄膜 | ASTMD882 | 10.0 | MPa |
| 薄膜 | 抗張強度 | TD:屈服,40μm,擠塑薄膜 | ASTMD882 | 9.00 | MPa |
| 薄膜 | 抗張強度 | MD:斷裂,40μm,擠塑薄膜 | ASTMD882 | 47.0 | MPa |
| 薄膜 | 抗張強度 | TD:斷裂,40μm,擠塑薄膜 | ASTMD882 | 49.0 | MPa |
| 薄膜 | 伸長率 | MD:斷裂,40μm,擠塑薄膜 | ASTMD882 | 630 | % |
| 薄膜 | 伸長率 | TD:斷裂,40μm,擠塑薄膜 | ASTMD882 | 700 | % |
| 薄膜 | 落錘沖擊2(40μm,鑄造薄膜) | ASTMD1709 | 700 | g | |
| 薄膜 | 埃爾曼多夫抗撕強度 | MD:40μm,鑄造薄膜 | ASTMD1922 | 12 | g |
| 薄膜 | 埃爾曼多夫抗撕強度 | TD:40μm,鑄造薄膜 | ASTMD1922 | 25 | g |
| 熱性能 | 熔融溫度 | 內(nèi)部方法 | 113 | °C | |
| 光學性能 | 霧度(40.0μm,鑄造薄膜) | ASTMD1003 | 1.5 | % | |
| 補充信息 | CastFilmMeltTemperature | 250到300 | °C | ||